Wear resistant alumina ceramic weldable tile
Alumina ceramic weld-on tile
Alumina ceramic tile with ceramic plug and steel ferrule
Advantages:----Excellent abrasion resistance (Scuff resistance), its theoretic wear resistance is 170times of chrome steel and 260 times of manganese steel materials
----Good corrosion resistance (Anticorrosion)
----Easy application (Quick installation)
----long working life.
----Good impact resistance.
----Good thermal shock resistance. Smooth surface and good adherence resistance
>>> Ceramic tile liner sizes
| Alumina ceramic tile popular Sizes (Length*width*thickness ) |
| 100*100*20mm (4"x4"x3/4") |
| 150*100*13mm (6"x4"x1/2") |
| 150*100*15mm (6"x4"x5/8") |
| 150*100*20mm (6"x4"x3/4") |
| 150*100*25mm (6"x4"x1") |
| 150*100*50mm (6"x4"x2") |
| 150*50*25mm (6"x4"x1") |
| 100*75*25mm (4"x3"x1") |
| 120*80*20mm |
| 228*114*25mm |
| 114*114*25mm |
More sizes and customized size acceptable.
Chemshun ceramics afford the relative weldable steel cone and ceramic rod.
|
Advantages:Low wear loss and long working life.
Good impact resistance.
Good corrosion resistant
Good thermal shock resistance.
Smooth surface and good adherence resistance.
Quick installation and good service after sale.
Complicated shape and various size designed according to customers' demands.
Application:-As alumina ceramic wear-resisting lining of coal-electing equipment on coal industry
-Cements industries;
-As wear resistant alumina ceramic lining of fall funnel, lining of wear-resisting pipe and bender,
-As wear resistant alumina ceramic liner of material tranfer pipe and chute, etc, on steel industry.
-As wear ceramic liner for l thansfer equipment;
-As Alumina ceramic wear plates Inside and outside surface of powder separating equipment on iron and steel works;
-Ceramics, mines and other grinding equipment lining;
-Parts of equipment hermal and power plants;
-Grinding systems Mixer Application areas
-Separator systems chain conveyor
-Cyclones diffusor
-sinter slurry ducts
-Hooper High temperature cyclones
-Ventilator housing salt plants
Alumina ceramic tile property :
Al2O3 |
SiO2 |
CaO |
MgO |
Na2O |
| 92~93% |
3~6% |
1~1.6% |
0.2~0.8% |
0.1% |
Physical properties:
Specific gravity (g/cc) |
>3.60 |
| Apparent porosity (%) |
0 |
| Flexural Strength (20 degree centigrade, Mpa) |
334 |
| Compressive strength (20degree centigrade, Mpa) |
1770 |
| Rockwell hardness (kg/mm 2 ) |
918 |
| Vickers hardness (hv) |
>750 |
| Moh's hardness (scale) |
≥9 |
| Thermal Expansion (20-800degree centigrade, x10-6/degree centigrade) |
8.30 |
| Crystal Size (μm) |
1.3~3.0 |