Polyether Insole a-1005A/B-5305

  • Price:

    Negotiable

  • minimum:

  • Total supply:

  • Delivery term:

    The date of payment from buyers deliver within days

  • seat:

    Zhejiang

  • Validity to:

    Long-term effective

  • Last update:

    2017-09-21 14:42

  • Browse the number:

    118

Send an inquiries

Company Profile

Zhejiang Hengtaiyuan Polyurethane Co., Ltd.

By certification [File Integrity]

Contact:Mr. hengtaiyuan(Mr.)  

Email:

Telephone:

Area:Zhejiang

Address:Zhejiang

Website: http://hengtaiyuan.artstx.com/

Product details
Typical properties of PU matrix

Name of products

Appearance

Viscosity (mPa·s/40ºC)

Density (g·cm-3/40ºC)

Package(kg)
A-1005A
cream white liquid
500~800 1.01~1.02 18
B-5305
Yellowish Transparent liquid or waxy
300~600 1.08~1.2 20
Materials preheat
A-1001A: 50~60ºC2~4 preheated at 50~60ºC for 2~4 hours
B-5301: 60~70ºC10~15 preheated at 60~70ºC for 10~15 hours
Typical processing parameters & Reaction parameter

 
Items

A/B Materials Temperatures
(ºC)

A+C/B Mix ratio
(By weight)

Cream Time (s)

End of Rise Time (s)

Free Rise Foam Density(g/cm3)

Mold Temperature(ºC)
Demold Time(min)

Parameter
30~35/35~40 100/45~47 7~9 50~60 0.13~0.16 45~55 3~5
Catalyst380g±20g/18kg The adding content of Catalyst should be 380g±20g/18kg
0~90g/18kg The adding content of water should be 0~90g/18kg according to the reality
0~600g/18kg The adding content of water should be 0~600g/18kg according to the reality
Physical properties

Items

Molded Density (g/cm3)

Hardness
(Shore C )

Tensile strength
(MPa)

Elongation (%)

Tear Strength
(kN/m)

168, 70ºC,95%
168h, 70ºC, 95%r.h. hydrolysis
strength retention(%)

Physical properties
0.28~0.50 28~50 2.0~5.0 300~380 18~26 >90
.
Demold time may be prolonged with the increase of sole thickness
6mm
These physical data are acquired by testing a sample of 6mm thick.